Bearing seat in the use of mechanical equipment is very prone to wear, slight wear may not directly affect the normal use, but if the use of a long time will lead to more serious wear, then the use of the effect will certainly be affected. So what are the consequences of bearing chamber wear? Can it still be repaired?

What are the consequences of bearing chamber wear?

Bearing chamber wear will cause the bearing to run the outer ring, and the bearing running the outer ring has a very large negative impact on the equipment, aggravate the wear of matching parts, and even scrap, damage the equipment, reduce the accuracy of the machine, in addition, increase the friction force, convert a lot of energy into useless heat and noise, reduce efficiency.

What are the consequences of bearing chamber wear? Can it still be repaired? Can bearing room wear be repaired and used?

For the bearing chamber wear is serious, it can be repaired and used. It is the use of Solay carbon nano-polymer material technology for repair, the use of reference scraping process, the use of unworn surface as the reference scraping, the use of bearing components corresponding relationship repair process for field repair. Under normal circumstances, bearing chamber wear can be repaired by this process. Let's take a look at an enterprise's vertical grinding bearing room wear repair case steps:

1. Use oxygen acetylene to dry the oil on the surface of the bearing seat, then use an Angle grinder or sandpaper to polish the surface oxidation layer clean and rough, and then clean the surface with anhydrous ethanol and dry;

2. Harmonize SD7101H material in strict accordance with proportion, harmonize uniformly without color difference;

3. Evenly apply the blended material to the bearing seat wear part, and the thickness of the coating is greater than the unilateral wear amount of the bearing seat;

4. Take the unworn parts on both sides of the shaft wear part as the benchmark for scraping to repair the benchmark size;

5. Material curing, the base surface and repair surface excess material and glaze with sandpaper to remove;

6. Apply SD7000 release agent to the bearing inner ring surface with clean cotton yarn, then apply a small amount of SD7101H material to the scraped surface, and install the bearing in place;

7. Apply a small amount of material again to the scraped surface, place the bearing oil hole upward, align the bearing position positioning step, and slowly drop into place;

8. The material is cured and the repair is complete.